Experimental characterization and finite element investigation of SiO2 nanoparticles reinforced dental resin composite.

In this study, a commercial dental resin was reinforced by SiO2 nanoparticles (NPs) with different concentrations to enhance its mechanical functionality. The material characterization and finite element analysis (FEA) have been performed to evaluate the mechanical properties. Wedge indentation and 3-point bending tests were conducted to assess the mechanical behavior of the prepared nanocomposites. The results revealed that the optimal content of NPs was achieved at 1% SiO2, resulting in a 35% increase in the indentation reaction force. Therefore, the sample containing 1% SiO2 NPs was considered for further tests. The morphology of selected sample was examined using field emission scanning electron microscopy (FE-SEM), revealing the homogeneous dispersion of SiO2 NPs with minimal agglomeration. X-ray diffraction (XRD) was employed to investigate the crystalline structure of the selected sample, indicating no change in the dental resin state upon adding SiO2 NPs. In the second part of the study, a novel approach called iterative FEA, supported by the experiment wedge indentation test, was used to determine the mechanical properties of the 1% SiO2-dental resin. Subsequently, the accurately determined material properties were assigned to a dental crown model to virtually investigate its behavior under oblique loading. The virtual test results demonstrated that most microcracks initiated from the top of the crown and extended through its thickness.

Differences in birch tar composition are explained by adhesive function in the central European Iron Age.

Birch bark tar is the most widely documented adhesive in prehistoric Europe. More recent periods attest to a diversification in terms of the materials used as adhesives and their application. Some studies have shown that conifer resins and beeswax were added to produce compound adhesives. For the Iron Age, no comparative large-scale studies have been conducted to provide a wider perspective on adhesive technologies. To address this issue, we identify adhesive substances from the Iron Age in north-eastern France. We applied organic residue analysis to 65 samples from 16 archaeological sites. This included residues adhering to ceramics, from vessel surface coatings, repaired ceramics, vessel contents, and adhesive lumps. Our findings show that, even during the Iron Age in north-eastern France, birch bark tar is one of the best-preserved adhesive substances, used for at least 400 years. To a lesser extent, Pinaceae resin and beeswax were also identified. Through statistical analyses, we show that molecular composition differs in samples, correlating with adhesive function. This has implications for our understanding of birch bark tar production, processing and mode of use during the Iron Age in France and beyond.

Evaluation of Microbiological Susceptibility and Long-term Adhesive Properties to Dentin of Primers with Terminalia catappa Linn.

PURPOSE: To investigate the antibacterial effects of Terminalia catappa Linn (TCL) leaf extracts at different concentrations and the effects of these extracts used as primers on the long-term adhesive properties of two universal adhesives. MATERIALS AND METHODS: After extract preparation, the antimicrobial and antibacterial activities of TCL against Streptococcus mutans (UA 159) were assessed in microdilution assays to provide the minimal inhibitory concentration (MIC) and minimal bactericidal concentration (MBC). Additionally, to provide quantitative data on the ability of TCL extract to reduce cell viability, colony forming units (CFU) were counted. To examine adhesive properties, 288 human molars were randomly assigned to 32 experimental conditions (n = 9) according to the following variables: (1) treatment agent: negative control (untreated surface), and primers at concentrations of 1xMIC, 5xMIC, and 10xMIC; (2) adhesives: Scotchbond Universal (SBU) and Futurabond Universal (FBU); (3) adhesive strategy: etch-and-rinse (ER) or self-etch (SE); and (4) storage time: 24 h or after 2 years. Primers were applied for 60 s, upon which the teeth were incrementally restored and sectioned into adhesive-dentin bonded sticks. These were tested for microtensile bond strength (µTBS) and nanoleakage (NL) after 24-h and 2-year water storage, as well as in-situ degree of conversion (DC) at 24 h. The chemical profile of the hybrid layer was determined via micro-Raman spectroscopy. Biofilm assay data were analyzed using the Kruskal-Wallis test; the pH of culture media and the chemical profile were analyzed by one-way ANOVA. The adhesive properties (µTBS, NL, DC) were evaluated using a four-way ANOVA and Tukey's test. Significance was set at 5%. RESULTS: Similar values of MIC and MBC were observed (2 mg/ml), showing bactericidal potential. CFU analysis demonstrated that concentrations of 5xMIC and 10xMIC significantly inhibited biofilm formation (p < 0.001). The application of the TCL primer at all concentrations significantly increased the immediate µTBS and DC, and decreased the immediate NL values when compared to the control group (p < 0.05), regardless of the adhesive and adhesive strategies. Despite an increase in the NL values for all groups after 2 years (p > 0.05), in groups where the TCL primer was applied, the µTBS remained constant after 2 years for both adhesives, while a decrease in the µTBS was observed in the control groups (p < 0.05). Usually, 10xMIC showed better results than 1xMIC and 5xMIC (p < 0.05). The application of TCL promoted cross-linking; cross-linking rates increased proportionally to the concentration of TCL (p < 0.05). CONCLUSION: Primers containing TCL promoted bactericidal and bacteriostatic action, as well as cross-linking with dentin, while maintaining the adhesive properties of the adhesive-dentin interface after 2 years of water storage.

A Novel Concept for Developing a Precise and Predictable Post and Core Complex Using the Injectable Resin Technique (Part 2).

Post and core systems have long been used in dentistry for the purposes of replacing missing coronal tooth structure, retaining the core, and providing sufficient retention and resistance form to the final restoration to re-establish original form and function. While Part 1 of this two-part article provided a history of post and core systems and materials and discussed empirical data regarding fiber-reinforced post systems, this second part of the article focuses on an alternative approach for developing a fiber-reinforced post and core system using a monoblock system via the injectable resin technique and a recently developed fiber-optic post. The present article explains the concept of a ferrule effect and demonstrates the novel restorative procedure.

Effect of Surface Treatment with Alkaline Agents at Two Different Temperatures on Microshear Bond Strength of Zirconia to Composite Resin.

Background: Zirconia, with its excellent mechanical properties, has become a popular choice for esthetic and durable restorations due to the increasing demand of patients. It has overcome most of the limitations of all ceramic restorations. However, bonding to zirconia remains a challenge. Objectives: This study is aimed at assessing the effect of surface treatment with alkaline agents at two different temperatures on microshear bond strength (µSBS) of zirconia to composite resin. Materials and Methods: This in vitro, experimental study was conducted on zirconia blocks measuring 2 × 4 × 8 mm. The blocks were sandblasted with alumina powder and randomly assigned to 5 groups (n = 16 each). The blocks in groups 1 and 2 underwent surface treatment with sodium hydroxide (NaOH) and groups 3 and 4 with zirconium hydroxide (Zr(OH)4) at room temperature and 70°C. Group 5 served as the control group and did not receive any surface treatment. After the application of bonding agent and its light-curing, composite cylinders in plastic tubes were bonded to the surface of each block and cured. After incubation, they underwent µSBS test. Data were analyzed by one-way ANOVA and Tukey's test (alpha = 0.05). Results: The µSBS was significantly higher in all intervention groups than that in the control group (P < 0.05). The µSBS in Zr(OH)4 groups was significantly higher than that in NaOH groups (P < 0.05). The mean µSBS of heated groups was slightly, but not significantly, higher than the corresponding room temperature groups (P > 0.05). Conclusion: Surface treatment of zirconia with NaOH and Zr(OH)4 alkaline agents can increase its µSBS to composite resin; Zr(OH)4 was significantly more effective than NAOH for this purpose, but heating did not have a significant effect on µSBS.

The Effect of Different Ageing Protocols on the Shear Bond Strength of the Ceromer Indirect Composite on Two Different Substructure Materials.

BACKROUND: The evolution of restorative materials in prosthodontics has led to the emergence of indirect composite resins, including ceromers, as alternatives to traditional metal-ceramic restorations. However, research gaps exist regarding the impact of ageing protocols on the bond strength of ceromer composites to different metal substructures, necessitating further investigation in this area. AIM: This study aimed to determine the effect of five different ageing protocols on the shear bond strength (SBS) of ceromer indirect composites on two different substructures. METHODS: In this in vitro study, 120 metallic discs (10 × 2 mm) were cast from cobalt-chromium (Co-Cr) alloy (n = 60) and spark erosion treated from grade V titanium (n = 60). Each sample was sandblasted. The M.L. primer (Shofu, Germany) and layers of opaque were applied to the surface following the manufacturer's instructions. A special jig (6 × 2 mm) was placed on each disc. The ceromer was condensed in it and light-cured separately for 90 s. Following polishing, specimens were separated into five ageing groups: distilled water (as a control), thermal cycling, tea, coffee, and gastric acid immersion. All samples were placed in 37°C incubation for 28 days for distilled water, coffee, and tea, and 7 days for gastric acid immersion and thermal cycling for 5000 cycles (5-55°C). A universal test machine was used to measure the SBS. The samples were evaluated for failure modes using stereomicroscopy. Data were analyzed using one-way analysis of variance (ANOVA) (P < 0.05). RESULTS: According to one-way ANOVA, the mean SBS (MPa) between the two groups was compared in each ageing protocol, and there were no significant differences between the Co-Cr-C and Ti-C groups (P > 0.05). The most frequent mode of failure in all groups was mixed. CONCLUSIONS: Applying the ageing protocols, the type of substructure material had no significant effect on the SBS of the ceromer indirect composite except for tea immersion.

Effect of chitosan and CMCS on dentin after Er:YAG laser irradiation: shear bond strength and surface morphology analysis.

OBJECTIVES: The aim of the present study was to evaluate the effect of chitosan and carboxymethyl chitosan (CMCS) on dentin surface morphology and bonding strength after irradiation of Er:YAG laser. METHODS: Eighty-four laser-irradiated dentin samples were randomly distributed into three groups (n = 28/group) according to different surface conditioning process: deionized water for 60s; 1wt% chitosan for 60s; or 1wt% CMCS for 60s. Two specimens from each group were subjected to TEM analysis to confirm the presence of extrafibrillar demineralization on dentin fibrils. Two specimens from each group were subjected to morphological analysis by SEM. Seventy-two specimens (n = 24/group) were prepared, with a composite resin cone adhered to the dentin surface, and were then randomly assigned to one of two aging processes: storage in deionized water for 24 h or a thermocycling stimulation. The shear bond strength of laser-irradiated dentin to the resin composite was determined by a universal testing machine. Data acquired in the shear bond strength test was analyzed by one-way ANOVA with the Tukey honestly significant difference post hoc test and Independent Samples t-test (α = 0.05). RESULTS: CMCS group presented demineralized zone and a relatively smooth dentin surface morphology. CMCS group had significantly higher SBS value (6.08 ± 2.12) without aging (p < 0.05). After thermal cycling, both chitosan (5.26 ± 2.30) and CMCS group (5.82 ± 1.90) presented higher bonding strength compared to control group (3.19 ± 1.32) (p < 0.05). Chitosan and CMCS group preserved the bonding strength after aging process (p > 0.05). CONCLUSIONS: CMCS has the potential to be applied in conjunction with Er:YAG laser in cavity preparation and resin restoration.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Adhesion of tooth fragment after trauma: effect of adhesion strategy and storage in the rescue box.

This study aims to investigate the impact of storage conditions for crown fragments (specifically, whether they were stored within a tooth rescue box or in tap water) on their adhesion to fractured teeth when subjected to two different adhesive systems (namely, total etch and self etch). Sixty maxillary premolars were sectioned to obtain tooth fragments. These fragments were stored briefly (2 hours) and reattached in the following groups: Group 1 (fragments stored in tooth rescue box and reattached with etch and rinse (E&R) technique), Group 2 (fragments stored in tap water and reattached with E&R technique), Group 3 (fragments stored in tooth rescue box and reattached with self-etch (SE) technique), and Group 4 (fragments stored in tap water and reattached SE technique). After reattachment, the bonded tooth fragments underwent thermal cycling (500 cycles, 5-55 °C) and bond strength testing using a universal testing machine. Two-way Analysis of Variance (ANOVA) and Tukey's tests were used for bond strength comparison (p ≤ 0.05). A two-parameter Weibull distribution was conducted to evaluate the reliability of the storage medium and adhesion modality on bond strength. The results showed that measured shear bond values (MPa ± Standard deviation (SD); arranged in descending order) for each group were: Group 2 (Tap water/E&R = 6.5 ± 2.1), Group 1 (Rescue box/E&R = 6.0 ± 2.5), Group 4 (Tap water/E&R = 5.1 ± 2.8), and Group 3 (Rescue box/SE = 3.6 ± 3.2). Significant differences were found only between Groups 2 and 3 (p = 0.002). In conclusion, storing crown fragments in a tooth rescue box did not significantly affect the shear bond strength of the restored tooth. However, fragments reattached using the self-etch technique showed comparable shear bond strength but a higher rate of adhesive failures compared to the E&R technique.

Componeer as an aesthetic treatment option for anterior teeth: a case report.

INTRODUCTION: Structural abnormalities or anomalies in the anterior teeth, also known as the aesthetic zone, are an important problem for patients and a challenge for dentists. Structural abnormalities or tooth anomalies can change in color, shape, and function. Most dentists prefer minimally invasive aesthetic treatment. One of the aesthetic treatment options for anterior teeth is veneers. Veneer is a restoration that covers the labial part of the tooth with a thin layer of material to correct abnormalities in the color, shape, or function of the tooth. Veneer restoration can be done indirectly with porcelain material made in a laboratory and directly with composite material on the tooth surface or prefabricated which is available from the factory. Componeer is a prefabricated composite veneer that combines the aesthetic properties of ceramic veneers and the adhesive ability of composite veneers to the tooth structure. This case report describes the treatment of two central incisors that had been filled with composite and peg shapes on both lateral incisors using a componeer. CASE REPORT: A 32-year-old female patient came to the Dental Conservation Clinic at Dentistry Hospital, Padjadjaran University with the main complaint of her right and left upper front teeth and wanted to repair her old fillings and close the gap between her right and left upper front teeth and her canine teeth. Clinical examination showed that teeth 11 and 21 had been filled with composite which had changed color and had an inharmonious shape as well as a gap between the upper front teeth on the right and left sides and the right and left canine teeth. TREATMENT: The maxilla and mandibular teeth are molded for study models and working models. In the working model, a wax-up is carried out, then a mock-up on the patient's teeth. Next, choose the color and size of the components that match the mock up results. Teeth 11 and 21 had their old composite fillings cleaned and refilled with dentin colored composite, teeth 13, 12, 11, 21, 22, and 23 were prepared with a minimum thickness of 0.3 mm to make room for the componeer material. The teeth was etched and bonded, and bonding was applied to the inner surface of the componeer. The composite is placed on the inner surface of the componeer then placed on the labial surface of the tooth and pressed with a special tool, then light cured. The final step is polishing. TREATMENT RESULTS: Teeth 13, 12, 11, 21, 22, and 23 which had undergone veneer treatment using componeer, were controlled after 1 week of treatment. The patient did not complain about the results of the treatment and said he was satisfied with the treatment.

Influence of printing orientation on mechanical properties of aged 3D-printed restorative resins.

OBJECTIVE: To evaluate the influence of printing orientation on flexural strength (σf) and elastic modulus (E) of different 3D printing dental restorative resins. METHODS: Bar-shaped specimens (n = 20) were fabricated from two SLA-printed resins (FT- Formlabs Temporary, and FP- Formlabs Permanent) and two DLP-printed resins (DFT- Detax Freeprint Temp, and GCT- GC Temporary) using two building orientations (0º and 90º). The 3D-printed structures were aged (14 d) before submitted to three-point bending in 37ºC distilled water at a crosshead speed of 1.0 ± 0.3 mm/min until fracture to calculate the σf and the E values. The fractured surfaces were evaluated using stereomicroscopy and scanning electron microscopy (SEM) following fractography principles. Data were statistically analyzed using two-way ANOVA and Tukey post-hoc (α = 0.001). RESULTS: FP and FT showed significantly higher E values than DFT and GCT, irrespectively of printing orientation (p < 0.001). There was no statistical difference between the building orientations (0º and 90º) for the mean σf and E values for the resin materials evaluated. Fractographic characteristics were similar for the surface fracture from all the materials evaluated, showing typical brittle fracture behavior. SIGNIFICANCE: Printing orientation did not influence of flexural strength and elastic modulus values for the 3D-printed resin structures evaluated. Surface topography was mostly governed by the 3D printer type.

Comparative analysis of stress distribution in residual roots with different canal morphologies: evaluating CAD/CAM glass fiber and other post-core materials.

BACKGROUND: The selection of post-core material holds significant importance in endodontically treated teeth, influencing stress distribution in the dental structure after restoration. The use of computer-aided design/computer-aided manufacturing (CAD/CAM) glass fiber post-core possesses a better adaptation for different root canal morphologies, but whether this results in a more favorable stress distribution has not been clearly established. MATERIALS AND METHODS: This study employed finite element analysis to establish three models of post-core crown restoration with normal, oversized, and dumbbell-shaped root canals. The three models were restored using three different materials: CAD/CAM glass fiber post-core (CGF), prefabricated glass fiber post and resin core (PGF), and cobalt-chromium integrated metal post-core (Co-Cr), followed by zirconia crown restoration. A static load was applied and the maximum equivalent von Mises stress, maximum principal stress, stress distribution plots, and the peak of maximum displacement were calculated for dentin, post-core, crown, and the cement acting as the interface between the post-core and the dentin. RESULTS: In dentin of three different root canal morphology, it was observed that PGF exhibited the lowest von Mises stresses, while Co-Cr exhibited the highest ones under a static load. CGF showed similar stress distribution to that of Co-Cr, but the stresses were more homogeneous and concentrated apically. In oversized and dumbbell-shaped root canal remnants, the equivalent von Mises stress in the cement layer using CGF was significantly lower than that of PGF. CONCLUSIONS: In oversized root canals and dumbbell-shaped root canals, CGF has shown good performance for restoration of endodontically treated teeth. CLINICAL RELEVANCE: This study provides a theoretical basis for clinicians to select post-core materials for residual roots with different root canal morphologies and should help to reduce the occurrence of complications such as root fracture and post-core debonding.

Shear Bond Strength to Enamel, Mechanical Properties and Cellular Studies of Fiber-Reinforced Composites Modified by Depositing SiO2 Nanofilms on Quartz Fibers via Atomic Layer Deposition.

Introduction: Poor interfacial bonding between the fibers and resin matrix in fiber-reinforced composites (FRCs) is a significant drawback of the composites. To enhance the mechanical properties of FRC, fibers were modified by depositing SiO2 nanofilms via the atomic layer deposition (ALD) technique. This study aims to evaluate the effect of ALD treatment of the fibers on the mechanical properties of the FRCs. Methods: The quartz fibers were modified by depositing different cycles (50, 100, 200, and 400) of SiO2 nanofilms via the ALD technique and FRCs were proposed from the modified fibers. The morphologies, surface characterizations of nanofilms, mechanical properties, and cytocompatibility of FRCs were systematically investigated. Moreover, the shear bond strength (SBS) of FRCs to human enamel was also evaluated. Results: The SEM and SE results showed that the ALD-deposited SiO2 nanofilms have good conformality and homogeneity. According to the results of FTIR and TGA, SiO2 nanofilms and quartz fiber surfaces had good chemical combinations. Three-point bending tests with FRCs showed that the deposited SiO2 nanofilms effectively improved FRCs' strength and Group D underwent 100 deposition cycles and had the highest flexural strength before and after aging. Furthermore, the strength of the FRCs demonstrated a crescendo-decrescendo tendency with SiO2 nanofilm thickness increasing. The SBS results also showed that Group D had outstanding performance. Moreover, the results of cytotoxicity experiments such as cck8, LDH and Elisa, etc., showed that the FRCs have good cytocompatibility. Conclusion: Changing the number of ALD reaction cycles affects the mechanical properties of FRCs, which may be related to the stress relaxation and fracture between SiO2 nanofilm layers and the built-up internal stresses in the nanofilms. Eventually, the SiO2 nanofilms could enhance the FRCs' mechanical properties and performance to enamel by improving the interfacial bonding strength, and have good cytocompatibility.

Evaluation of mechanical properties of anatomically customized fiber posts using E-glass short fiber-reinforced composite to restore weakened endodontically treated premolars.

OBJECTIVE: This study was conducted to assess the influence of combining different forms of fiber-reinforced composites (FRC) on the mechanical behavior and bond strength of compromised endodontically treated teeth (ETT). MATERIALS AND METHODS: Eighty extracted human premolar teeth were randomly divided into five experimental groups according to the type of intra-radicular restoration and the canal preparation design which was either non-flared (Group 1), flared (Groups 2-5), closed-apex (Groups 1,3,5) or open-apex (Groups 2,4). Standard prefabricated fiber posts were used as intra-radicular restoration for Groups 1-3 while Groups 4-5 were restored with anatomically customized relined fiber posts. After composite core fabrication, all samples were sent for an artificial aging process. Fracture resistance and push-out bond strength tests were then carried out through a universal testing machine followed by mode of failure analysis via a stereomicroscope and scanning electron microscope. RESULTS: Pairwise Log-Rank comparisons revealed that the survival rate of Group 2 and Group 3 was significantly lower than all other groups after artificial aging. The highest fracture resistance value (1796 N) was recorded in Group 5 and was significantly higher than that of the other groups (p < 0.05), while Group 2 exhibited the lowest fracture resistance (758 N), which was significantly lower compared to the other groups. Group 5 and Group 4 demonstrated a significantly higher push-out bond strength, at all root thirds, than Group 3, Group 2, and Group 1 (p < 0.05). The most frequently observed failure mode in the tested groups occurred between the resin cement and radicular dentin. CONCLUSION: The use of short fiber-reinforced composite (SFRC) to reline the prefabricated FRC post has been proven to have superior fracture resistance with favorable failure patterns and increased push-out bond strength values compared to standard prefabricated FRC posts.

Evaluation of the Mechanical Properties of 3D-Printed Post and Core Systems.

PURPOSE: To evaluate and compare the fracture resistance and elastic modulus of 3D-printed post and core systems and fiber posts and composite cores. MATERIALS AND METHODS: Endodontic treatment was performed on 30 mandibular premolars, and post space preparation was performed. The teeth were then randomly divided into two groups (n = 15 per group): the 3D-printed (3DP) group and the fiber post and composite core (FPC) group. In the FPC group, fiber posts (Cytec Blanco 43.604, Hahnenkratt) were bonded with resin cement (RelyX U200, 3M), and the composite core dimension was standardized with a silicone index. In the 3DP group, the impression of the post space for each specimen was taken with pattern resin (Pattern Resin, GC America), and the coronal core was produced with the same silicone index. The impressions of the posts and cores were scanned, and then the custom post and core structures were fabricated from permanent crown resin material (Permanent Crown Resin, Formlabs) with a 3D printer (Form3B, Formlabs). Specimens were subjected to load tests with a universal testing machine (M500-25AT, Testometric). After fracture occurred, the fracture force and elastic modulus were calculated. The data were analyzed by independent sample t test (α = .05) Results: There was no statistically significant difference between the two groups in terms of peak fracture force (P = .626) and elastic modulus (P = .125), and no catastrophic root fractures were observed in either group. CONCLUSIONS: The fracture resistance of endodontically treated teeth was not significantly influenced by the post material. 3D-printed, custom-made resin posts were as effective as fiber glass posts with regard to fracture resistance.

Characterisation of experimental flowable composites containing fluoride-doped calcium phosphates as promising remineralising materials.

OBJECTIVE: Remineralising composites with antibacterial properties may seal the cavity and prevent secondary caries. This study aimed at developing experimental flowable composites containing different concentrations of fluoride-doped calcium phosphate fillers and evaluating their remineralising and antibacterial properties. METHODS: Experimental resin-based composites containing different concentrations (0-20 %) of fluoride-doped calcium phosphate fillers (VS10/VS20) were formulated. The release of calcium (Ca), phosphate (PO) and fluoride (F) ions was assessed for 30 days. Remineralisation properties were evaluated through ATR-FTIR and SEM/EDX after storage in simulated body fluid (SBF). The metabolic activity and viability of Streptococcus gordonii was also evaluated through ATP, CFU and live/dead confocal microscopy. The evaluation of specific monomer elution from the experimental composites was conducted using high-performance liquid chromatography (HPLC). RESULTS: The composites containing VS10 showed the highest release of Ca, those containing VS20 released more F over time (p < 0.05), while there was no significant difference in terms of PO ions release between the groups (p > 0.05). A quick 7-day mineral precipitation was observed in the tested composites containing VS10 or VS20 at 10 %; these materials also showed the greatest antibacterial activity (p < 0.05). Moreover, the tested composites containing VS10 presented the lowest elution of monomers (p < 0.05). CONCLUSIONS: Innovative composites were developed with low monomers elution, evident antibacterial activity against S. gordonii and important remineralisation properties due to specific ions release. CLINICAL SIGNIFICANCE: Novel composites containing fluoride-doped calcium phosphates may be promising to modulate bacteria growth, promote remineralisation and reduce the risk of cytotoxicity related to monomers' elution.

Promoting bond durability by a novel fabricated bioactive dentin adhesive.

OBJECTIVE: To prepare a bioactive dentin adhesive and investigate its effect on promoting bonding durability of dentin. METHODS: The mineralization of the bioactive glass with high phosphorus (10.8 mol% P2O5-54.2 mol% SiO2-35 mol% CaO, named PSC) and its ability to induce type I collagen mineralization were observed by SEM and TEM. The Control-Bond and the bioactive dentin adhesive containing 20 wt% PSC particles (PSC-Bond) were prepared, and their degree of conversion (DC), microtensile bond strength (µTBS), film thickness and mineralization performance were evaluated. To evaluate the bonding durability, dentin bonding samples were prepared by Control-Bond and PSC-Bond, and mineralizated in simulated body fluid for 24 h, 3 months, and 6 months. Then, the long-term bond strength and microleakage at the adhesive interface of dentin bonding samples were evaluated by microtensile testing and semiquantitative ELIASA respectively. RESULTS: The PSC showed superior mineralization at 24 h and induced type I collagen mineralization to some extent under weakly alkaline conditions. For PSC-Bond, DC was 62.65 ± 1.20%, µTBS was 39.25 ± 4.24 MPa and film thickness was 17.00 ± 2.61 µm. PSC-Bond also formed hydroxyapatite and maintained good mineralization at the bonding interface. At 24 h, no significant differences in µTBS and interface microleakage were observed between the Control-Bond and PSC-Bond groups. After 6 months of aging, the µTBS was significantly higher and the interface microleakage was significantly lower of PSC-Bond group than those of Control-Bond group. SIGNIFICANCE: PSC-Bond maintained bond strength stability and reduced interface microleakage to some extent, possibly reducing the occurrence of secondary caries, while maintaining long-term effectiveness of adhesive restorations.

Validation of a human saliva model for the determination of leachable monomers and other chemicals from dental materials.

This study aimed to prove the validity of a mixture of chemicals, including salts, small organic molecules, mucin, and α-amylase, as saliva surrogate ("artificial saliva") for assessing leakage of methacrylate monomers and other constituents from dental materials. To achieve this, we developed and validated a liquid chromatography-tandem mass spectrometry (LC-MS/MS) method for the quantification of 2-hydroxyethyl methacrylate (HEMA), triethylene glycol dimethacrylate (TEGDMA), diurethane dimethacrylate (UDMA), bisphenol A glycerolate dimethacrylate (BisGMA), diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO), bisphenol A (BPA), and five homologues of ethoxylated bisphenol A dimethacrylate (BisEMA EO2-6) in unstimulated and artificial saliva, and compared their concentrations in the two saliva media following either spiking with a mixture of the compounds or incubation of test specimens of printed biomaterials. Test specimens were immersed in unstimulated/artificial saliva, incubated at 37 °C for 24 h, and saliva aliquots were extracted with methanol and subsequently analyzed by LC-MS/MS. The method was validated with regard to matrix effects, linearity, selectivity, lower limits of quantification (LLOQ), precision, bias and combined measurement uncertainty (u'). The performance characteristics of the method were comparable for unstimulated and artificial saliva samples. The combined u' for individual chemicals at a concentration of 10 × LLOQ were within the range of 5.3-14 % for unstimulated saliva and 6.9-16 % for artificial saliva, except for the BisEMA homologues. Combined u' for the latter were 27-74 % in unstimulated saliva, and 27-79 % in artificial saliva. There was no detectable release of BPA from the test specimens, and the TPO concentrations were mainly below the LLOQ. TEGDMA and UDMA were detected in the highest quantities, and at comparable concentrations in the unstimulated and artificial saliva. For all BisEMA homologues, the release was higher in unstimulated saliva than in artificial saliva. The study showed that the artificial saliva model can be a suitable replacement for native saliva, but might underestimate leakage of more lipophilic methacrylates.

Comparative Evaluation of Fracture Toughness and Flexural Strength of Four Different Core Build-up Materials: An In Vitro Study.

AIM: To evaluate and compare the fracture toughness and flexural strength of four different core build-up materials. MATERIALS AND METHODS: A total of 60 samples were divided into four groups (n = 15) group I: dual cure composite resin reinforced with zirconia particles (Luxacore Z), group II: light cure composite resin (Lumiglass DeepCure), group III: zirconia reinforced glass ionomer cement (GIC) (Zirconomer Improved), and group IV: chemically cure composite resin (Self Comp) respectively. All the core build-up materials were manipulated according to the manufacturer's instructions and poured into the mold. A universal testing machine applied a central load to the specimen in a 3-point bending mode. Fracture of the specimen was identified and the reading was recorded by the universal testing machine. The data were analyzed statistically using one-way analysis of variance (ANOVA) and then compared. RESULTS: Group I showed the highest flexural strength (48.65 MPa) among all the groups while group IV showed the lowest flexural strength (17.90 MPa). Group I showed the highest fracture toughness (99.12 MPa) among all the groups while group IV showed the lowest fracture toughness (36.41 MPa.cm-0.5). When mean flexural strength and fracture toughness values of all four groups were compared by using one-way ANOVA, the compared data was highly significant. CONCLUSION: Based on the findings of this study, dual cure composite resin was the material of choice in terms of flexural strength and fracture toughness for core build-up material followed by light cure composite resin. CLINICAL SIGNIFICANCE: The core buildup material serves to strengthen the tooth structure, allowing it to withstand the forces of chewing and preventing the risk of tooth fractures. This material is essential in restoring damaged or decayed teeth, as it provides a stable foundation for further dental work. By reinforcing the tooth structure, the core buildup material ensures that the tooth can function properly and remain healthy for years to come. How to cite this article: Nakade P, Thaore S, Bangar B, et al. Comparative Evaluation of Fracture Toughness and Flexural Strength of Four Different Core Build-up Materials: An In Vitro Study. J Contemp Dent Pract 2024;25(2):191-195.

Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus.

AIM: The aim of the present study was to evaluate the shear bond strength of resin-modified glass ionomer cement with two different types of mineral trioxide aggregate at different time intervals. MATERIALS AND METHODS: A total of 80 cylindrical blocks were prepared using a self-cure acrylic resin with a central cavity of 4 mm internal diameter and 2 mm height. The prepared samples were randomly divided into two groups (n = 40 each) according to the type of MTA cements used (ProRoot MTA and MTA Angelus). Two groups were further sub-divided into four sub-groups of 10 samples each according to the different time intervals. ProRoot MTA and MTA Angelus were placed in the prepared cavity and a wet cotton pellet was placed over the filled cavity. A hollow plastic tube was placed over the MTA surface and resin-modified glass ionomer cement (RMGIC) was placed into the hollow plastic tube and light-cured (Spectrum 800, Dentsply Caulk Milford, DE, USA) according to the time intervals decided. After light curing the plastic tubes were removed carefully and the specimens were stored at 37°C and 100% humidity for 24 hours to encourage setting of MTA. The specimens were mounted in a universal testing machine (ADMET) and a crosshead speed of 0.5 mm/min was applied to each specimen by using a knife-edge blade until the bond between the MTA and RMGIC failed. The data were statistically analyzed using ANOVA, post hoc Tukey's t-test and Fisher's t-test and p-value ≤ 0.5 was considered significant. RESULTS: For both ProRoot MTA and MTA Angelus there was no statistically significant difference between 45 minutes and 24 hours (p-value ≥ 0.8). For ProRoot MTA, shear bond strength value at 10 minutes were significantly lower than 45 minutes and 24 hours group. However, for MTA Angelus, shear bond strength value at 10 minute was not significantly different from 45 minutes group (p-value ≥ 0.3). For both ProRoot MTA and MTA Angelus shear bond strength value at 0 minute were the least and were significantly lower than 10 minutes, 45 minutes, and 24 hours, respectively (p-value ≥ 0.000). CONCLUSION: Resin-modified glass ionomer cement can be layered over MTA Angelus after it is allowed to set for 10 minutes. However, ProRoot MTA should be allowed to set for at least 45 minutes before the placement of RMGIC to achieve better shear bond strength. CLINICAL SIGNIFICANCE: Due to the variety of types of mineral trioxide aggregate cements available in dentistry, it is justifiable to emphasize on different time intervals as it may affect the shear bond strength of restorative cements. Such information is pivotal for the clinicians while using mineral aggregate-based cements that receive forces from the condensation of restorative materials or occlusion, as the compressive strength may be affected due to different time intervals. How to cite this article: Tyagi N, Chaman C, Anand S, et al. Comparative Evaluation of Shear Bond Strength of Resin-modified Glass Ionomer Cement with ProRoot MTA and MTA Angelus. J Contemp Dent Pract 2024;25(1):35-40.